钢结硬质合金的制备、组织与性能研究
摘要 钢结硬质合金是以钢为粘结相，难溶金属碳化物(主要有 WC、TiC 等)为硬质相的一种复合材料，其组织特点是微细硬质晶粒均匀分散于钢基体中,故兼有硬质化合物的硬度和耐磨性以及钢的强度和韧性。其力学性能介于硬质合金和钢之间，与钢相比，有更高的硬度、更好的耐磨性及更高的弹性模量和抗压强度；与硬质合金相比，有良好的抗弯强度和冲击韧性，表现出优异的综合性能，因此得到了广泛的应用。
关键词 钢结硬质合金；WC；TiC；机械性能；微观结构
Abstract
Steel bonded carbide is a kind of composite material used steel as binder and refractory metal carbides (mainly including WC, TiC,etc.) as hard phase , its organization is characterized by fine hard grain evenly dispersed in the steel matrix, so it has the hardness and wear resistance of hard compound as well as the strength and toughness of steel. Its mechanical properties is between cemented carbide and steel. Compared with steel, it has higher hardness,better wear resistance,higher elastic modulus and compressive strength.Compared with cemented carbide,it has higher bending strength and impact toughness showig excellent comprehensive performance.Therefore,it has been widely used.
Keywords：Steel bonded carbide ；WC ；TiC ；Mechanical properties ；Microstructure
1 引言
1.1 钢结硬质合金的发展概况
钢结硬质合金作为一种新型材料最早出现在美国,1955年C G格策尔等发表了制取可加工、可热处理的硬质合金的资料。同一时期,美国铬合金公司用浸渍和液相烧结的方法制取了钢结硬质合金Ferro -TiC。1963年,西德蒂森特殊钢厂生产了畅销至今的C特牌号。1970年荷兰菲利蒲灯泡有限公司的工具与机械制造厂研制并生产了十三种钢结硬质合金牌号[1]。我国钢结硬质合金发展的主要特点是TiC与WC两大系列同时发展,且其发展可归结为三个时期:1962～1966年为TiC系钢结合金研制时期[2];1967～1970年,WC系钢结合金开始研制;1970年以后,随着真空连续烧结炉的试制成功,TiC系钢结合金开始工业生产,产量不断提高,品种规格不断增加,同时,WC系钢结合金研制成功[3]。因WC钢结合金生产不需要真空设备,工艺简单,且我国钨资源丰富,故近年来WC系钢结合金在我国得到迅速发展。
以上是毕业论文文献综述，课题毕业论文、任务书、外文翻译、程序设计、图纸设计等资料可联系客服协助查找。